Gunning mixes are carefully designed refractories having instant adhesion to the surface and low rebond loss. These type of products suitable for hot and cold gunning. They are used through pneumatic guns or centrifugal fettling machines.
Gunning refractory, containing lower Fe2O3 and has an excellent resistance against thermal shock and impacts.
A hydraulic setting castable which has high abrasion-resistant.
Fire clay base, hydraulic setting low temperature hot or cold gunning or trowelling mix. Recommended for refineries or similar low temperature applications.
It's a SiC based hydraulic setting gunning castable which contains % 45 AI2O3. It has corrosion resistance and strength.
It is a gunning castable made of high quality chamotte, corundum and high alumina cement. It has good abrasion resistance, volume stability and no shrinkage at high temperature.
Fire clay base, chemical bonded hot and cold gunning mix for super duty surfaces. Especially recommended for Steel soaking pits, reheating furnaces etc.
70 Alumina, hydraulic-bonded gunning mix. Especially designed to withstand carbon monoxide atmospheres.
The material is applied as a hot gunning material on the erosed surface of the RH type vacuum snorkels.
Alumina-bauxite base, chemically bonded, high erosion and abrasion resistance material. Aluminum melting furnaces, Steel pelletizing furnace, hot metal mixers, hot sintering furnaces are typical applications.
90 Alumina, corundum base, chemical bonded, high erosion and abrasion resistance, low iron and alkali content material. Typical applications are similar to those of Hygun® 80 CH.
60 Alumina, 6% zirconium reinforced, gunning castable. Highly resitant to corrosion, deformation, friction and thermal shocks.
60 Alumina, 10 % zirconium reinforced, gunning castable. Highly resitant to corrosion, deformation, friction and thermal shocks.